Measurement Area 210 from 0010669_edx
Type: Volume Composition show more
ObjectId: 149890
Created: 10/16/2025 3:18:14 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]
Access: Public Sort Code (asc): 210
Description: Automatically created via import from file (MA 210)
[no file attached]
: Co-La-Ni-O
Composition
| Element | Absolute | Percentage | |
|---|---|---|---|
| O | 91.71 % | ||
| Co | 2.967 % | ||
| Ni | 1.235 % | ||
| La | 4.088 % |
Referenced Objects (Reverse Association)
-
10669 241106-K3-1
SampleLa-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto -
10670 241107-K3-1
SampleLa-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto -
10671 241108-K3-1
SampleLa-Co-V-O hot deposition 500°C on Si/SiO2 with Pt-electrode layer (50nm Pt on 10nm Ta, 240731-K7-1), La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto
All properties (except table)
| Type | Name | Value | Comment | |
|---|---|---|---|---|
| Int | Measurement Area | 210 | 115586 | |
| Float | x | 0.01 | 115586 | |
| Float | y | 9.03 | 115586 | |
| String | Phases | ICSD-17668 | 117090 | |
| Float | R | 3423.6 | Resistance (Room Temperature) for Measurement Area 210 | 115585 |
| Float | Bandgap | 3.07356 | eV | 150023 |
| Float | SDC Area | 0.00714 | cm² | 129048 |
| Float | SDC Current Density | 0.276539 | mA/cm² | 129048 |