Measurement Area 190 from 0010669_edx
Type: Volume Composition show more
ObjectId: 149870
Created: 10/16/2025 3:18:13 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]
Access: Public Sort Code (asc): 190
Description: Automatically created via import from file (MA 190)
[no file attached]
: Co-La-Ni-O
Composition
| Element | Absolute | Percentage | |
|---|---|---|---|
| O | 91.651 % | ||
| Co | 3.182 % | ||
| Ni | 1.099 % | ||
| La | 4.067 % |
Referenced Objects (Reverse Association)
-
10669 241106-K3-1
SampleLa-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto -
10670 241107-K3-1
SampleLa-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto -
10671 241108-K3-1
SampleLa-Co-V-O hot deposition 500°C on Si/SiO2 with Pt-electrode layer (50nm Pt on 10nm Ta, 240731-K7-1), La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h
Auto
All properties (except table)
| Type | Name | Value | Comment | |
|---|---|---|---|---|
| Int | Measurement Area | 190 | 115586 | |
| Float | x | 4.51 | 115586 | |
| Float | y | 4.53 | 115586 | |
| String | Phases | ICSD-17668 | 117090 | |
| Float | R | 4195.95 | Resistance (Room Temperature) for Measurement Area 190 | 115585 |
| Float | Bandgap | 1.80051 | eV | 150023 |
| Float | SDC Area | 0.00816 | cm² | 129048 |
| Float | SDC Current Density | 0.268899 | mA/cm² | 129048 |