Measurement Area 182 from 0010669_edx

Type: Volume Composition

ObjectId: 149862

Created: 10/16/2025 3:18:13 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Access: Public Sort Code (asc): 182

Description: Automatically created via import from file (MA 182)

[no file attached]

: Co-La-Ni-O

Composition

ElementAbsolutePercentage
O 92.096 %
Co 1.849 %
Ni 1.057 %
La 4.999 %

Associated Objects

No associated objects found.

Referenced Objects (Reverse Association)

  • 10669 241106-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10670 241107-K3-1
    Sample

    La-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10671 241108-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Si/SiO2 with Pt-electrode layer (50nm Pt on 10nm Ta, 240731-K7-1), La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto

All properties (except table)

Type Name Value Comment
Int Measurement Area 182 115586
Float x -31.49 115586
Float y 4.53 115586
String Phases ICSD-7795;ICSD-31584;ICSD-17668 117090
Float R -1.41105e+007 Resistance (Room Temperature) for Measurement Area 182 115585
Float Bandgap 2.24066 eV 150023
Float SDC Area 0.00648 cm² 129048
Float SDC Current Density 0.134692 mA/cm² 129048