Measurement Area 140 from 0010669_edx

Type: Volume Composition

ObjectId: 149820

Created: 10/16/2025 3:18:12 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Access: Public Sort Code (asc): 140

Description: Automatically created via import from file (MA 140)

[no file attached]

: Co-La-Ni-O

Composition

ElementAbsolutePercentage
O 93.079 %
Co 0.796 %
Ni 0.996 %
La 5.129 %

Associated Objects

No associated objects found.

Referenced Objects (Reverse Association)

  • 10669 241106-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10670 241107-K3-1
    Sample

    La-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10671 241108-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Si/SiO2 with Pt-electrode layer (50nm Pt on 10nm Ta, 240731-K7-1), La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto

All properties (except table)

Type Name Value Comment
Int Measurement Area 140 115586
Float x -31.49 115586
Float y -4.47 115586
String Phases ICSD-7795;ICSD-31584;ICSD-17668 117090
Float R -9.97709e+006 Resistance (Room Temperature) for Measurement Area 140 115585
Float Bandgap 2.35195 eV 150023
Float SDC Area 0.00659 cm² 129048
Float SDC Current Density 0.112994 mA/cm² 129048