: Co-La-Ni-O

Composition

ElementAbsolutePercentage
O 92.776 %
Co 1.454 %
Ni 1.506 %
La 4.264 %

Associated Objects

No associated objects found.

Referenced Objects (Reverse Association)

  • 10669 241106-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10670 241107-K3-1
    Sample

    La-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto
  • 10671 241108-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Si/SiO2 with Pt-electrode layer (50nm Pt on 10nm Ta, 240731-K7-1), La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

    Auto

All properties (except table)

Type Name Value Comment
Int Measurement Area 67 115586
Float x 4.51 115586
Float y -22.47 115586
String Phases ICSD-7795;ICSD-31584;ICSD-17668 117090
Float R 1.32667e+007 Resistance (Room Temperature) for Measurement Area 67 115585
Float Bandgap 2.2485 eV 150023
Float SDC Area 0.00689 cm² 129048
Float SDC Current Density 0.159896 mA/cm² 129048